#0 dbbase_sql->halt(Invalid SQL: update dev_news_con set cl=cl+1 where id='422') called at [D:\23.245.100\23.245.100.190\www.qdjkb.com\wwwroot\includes\db.inc.php:65] #1 dbbase_sql->query(update {P}_news_con set cl=cl+1 where id='422') called at [D:\23.245.100\23.245.100.190\www.qdjkb.com\wwwroot\news\module\NewsContent.php:82] #2 NewsContent() called at [D:\23.245.100\23.245.100.190\www.qdjkb.com\wwwroot\includes\common.inc.php:524] #3 PrintPage() called at [D:\23.245.100\23.245.100.190\www.qdjkb.com\wwwroot\news\html\index.php:15] HVOF喷涂纳米WC-12Co涂层的性能研究-青岛喷砂机|山东喷砂机|青岛冠泰喷砂机械有限公司
HVOF喷涂纳米WC-12Co涂层的性能研究
作者:管理员    发布于:2016-03-13 11:10:12    文字:【】【】【

 1.2HVOF喷涂试验两种粉末都是采用国产T1-13200CY型HVOF设备进行喷涂,此设备采用航空煤油作为燃料,氧气作为助燃气,送粉载气采用氮气,喷涂工艺参数见表1.两种材料各喷涂了5个拉伸试样,4块冲蚀试样及若干金相试样。喷涂前,试样要严格进行除锈、除油,然后采用240pm(60目)白刚玉砂进行粗化处理,涂层设计厚度为0.4mm,在特殊的夹具上一次装夹喷涂。

  由表1可以看出,在喷涂纳米材料的参数和喷涂常规粉末材料的参数略有不同,这主要是考虑到它们在焰流中的特性差异所致,其目的主要是防止纳米材料中WC粒子的氧化脱碳。

  表1粉末类型喷枪型号煤油流量/(L/h)氧气流量/(m3/h)氧气压力/MPa送粉率/(kg/h)喷涂距离/mm纳米长型微米长型1.3结合强度试验采用拉伸法在国产液压式万能试验机(WE-30)上进行涂层的结合强度试验,拉伸试验参照GBT8642-88标准进行。拉伸试样尺寸为25X30mm,试样结合面采用TS811型粘接剂粘接。粘接剂的调和、固化严格按产品说明操作。

  1.4显微硬度试验显微硬度试验的试样是在尺寸为50mmX 5mm的试样上通过线切割切下尺寸为10mmX14mmX5mm的小块,后经过镶嵌完成的。

  然后采用国产*71*型显微硬度计上进行试验,试验载荷为200g,压力保持时间为15s,在不同的层面上选取不同的5个点分别测量。

  1.5冲蚀及冲蚀磨损形貌检测试验冲蚀试样尺寸为80mmX60mmX3mm,采用GP-1型干式喷砂机,气体压力0.4MPa,冲蚀距离120mm,喷嘴直径8mm,磨料为198~124pm(80~120目)的铜矿砂,分别在30*和90*两种攻角下进行。最后采用精确度为0.1mg的TG328电子天平称重,以单位重量的用砂量(100g)下的冲蚀失重量,即冲蚀率大小来评定涂层耐冲蚀磨损性能。最后采用S-570型扫描电镜(SEM)观察比较两种涂层的微观结构和冲蚀磨损形貌,工作电压20kV,束流2试验结果及分析2.1力学性能拉伸结果如表2所示。试验结果表明,采用HVOF方法得到的WC-12Co涂层结合强度,采用胶结拉伸法只能对其做出定性的估算,不能得出定量的结果。